Idiwọn Idanwo (Q/BLD2007-04) |
Kuro |
Iye Aṣoju |
|
Ti ara | |||
Iwuwo |
1.50 |
g/cm3 |
1.45 |
Darí | |||
Agbara fifẹ |
≥48 |
Mpa |
50 |
Gigun |
≥10 |
% |
11 |
Agbara Ipa |
≥10 |
Mpa |
11 |
Gbona | |||
Vicat mímú otutu |
≥70 |
° C |
76.8 |
Ipaba otutu |
≥68 |
° C |
68 |
Kemikali | |||
35% ± 1% (v/v) HCI |
± 4 |
g/ cm2 |
+2 |
30% ± 1% (v/v) H2Nitorinaa4 |
± 3 |
g/ cm2 |
+1 |
40% ± 1% (v/v) HNO3 |
± 3 |
g/ cm2 |
+1 |
40% ± 1% (v/v) NaOH |
± 3 |
g/ cm2 |
+1 |
Awọn ọpa yika PVC ni a ṣe pẹlu resini wundia polyvinyl chloride (PVC), amuduro, lubricant, plasticizer, kikun, iyipada ipa, awọ ati aropo miiran. O jẹ pẹlu sooro tutu to dara, acid & sooro alkali, weldable ati ohun-ini egboogi-ibajẹ to dara. Yato si, ohun -ini ti ara rẹ dara julọ ju roba ati awọn ohun elo miiran ti a kojọpọ. O jẹ lilo pupọ ni ile -iṣẹ kemikali ati iṣelọpọ galvanization. Gẹgẹ bi awọ sẹẹli elekitirotiki, awọn edidi idabobo itanna, fifọ fifọ abbl.
Gígan gíga;
Idinku kekere;
Irisi lẹwa;
O tayọ formability;
Lile dada to gaju ;
Idabobo itanna to gbẹkẹle ;
O tayọ ibere sooro išẹ,
O tayọ kemikali ati ipata ipata;
Ipa ipa ati resistance si awọn nkan ti n ṣatunṣe kemikali;
Dayato išẹ.
ROHS.
Ile-iṣẹ wa gba awọn ohun elo aise ore-ayika. Ṣe iṣakoso ilana iṣelọpọ ni lile, lati awọn ohun elo aise si ayewo didara ile -iṣẹ.Iyẹwo idanwo wọnyi tẹle iṣakoso didara agbaye ati eto iwe -ẹri lati rii daju didara awọn ọja.
Ile -iṣẹ wa ṣeto nọmba kan ti awọn adanwo ominira, pẹlu iwọn giga ti adaṣiṣẹ ti ẹrọ iṣelọpọ, ni gbogbo ọdun lati nawo owo pupọ, iṣafihan talenti ati imọ -ẹrọ, ni agbara iwadii ijinle to lagbara.
Awọn ọpa yika PVC ti ni lilo pupọ ni iṣelọpọ ti imi imi -ọjọ, aabo ayika ati epo, ile -iṣẹ kemikali, ati ninu okun kemikali, ile elegbogi, alawọ, awọ, bii ile -iṣẹ iṣelọpọ tun ti jẹ nọmba nla ti awọn ohun elo.